The purification of hydrogen gas is possible by diffusion through a thin palladium sheet. Calculate the number of kilograms of hydrogen that pass per hour through a 4.0-mm-thick sheet of palladium having an area of 0.13 m2 at 500°C. Assume a diffusion coefficient of 5.1 × 10-8 m2/s, that the concentrations at the high- and low-pressure sides of the plates are 2.9 and 0.31 kg/m3 of hydrogen per cubic meter of palladium, and that steady-state conditions have been attained.

A3-mm-thick panel of aluminum alloy (k 177 w/m-k, c 875 j/kg-k and ? = 2770 kg/m) is finished on both sides with an epoxy coating that must be cured at or above t,-150°c for at least 5 min. the production line for the curing operation involves two steps: (1) heating in a large oven with air at ts,0-175°c and a convection coefficient of h, 40 w/m2. k, and (2) cooling in a large chamber with air at 25°c and a con- vection coefficient of he 10 w/m2.k. the heating portion of the process is conducted over a time interval te which exceeds the ime required to reach 150°c by 5 min (h = r + 300 s). the coating has an emissivity of ? = 0.8, and the temperatures of the oven and chamber walls are 175 and 25°c, respectively. if the panel is placed in the oven at an initial temperature of 25°c and removed from the chamber at a safe-to-touch tempera ture of 37°c, what is the total elapsed time for the two-step curing operation?