Carbon is allowed to diffuse through a steel plate 9.4-mm thick. The concentrations of carbon at the two faces are 0.950 and 0.399 kg of carbon per m3 of iron, which are maintained constant. If the pre exponential and activation energy are 6.5 x 10-7 m2/s and 82 kJ/mol, respectively, calculate the temperature (in K) at which the diffusion flux is 3.2 x 10-9 kg/(m2-s).

A3-mm-thick panel of aluminum alloy (k 177 w/m-k, c 875 j/kg-k and ? = 2770 kg/m) is finished on both sides with an epoxy coating that must be cured at or above t,-150°c for at least 5 min. the production line for the curing operation involves two steps: (1) heating in a large oven with air at ts,0-175°c and a convection coefficient of h, 40 w/m2. k, and (2) cooling in a large chamber with air at 25°c and a con- vection coefficient of he 10 w/m2.k. the heating portion of the process is conducted over a time interval te which exceeds the ime required to reach 150°c by 5 min (h = r + 300 s). the coating has an emissivity of ? = 0.8, and the temperatures of the oven and chamber walls are 175 and 25°c, respectively. if the panel is placed in the oven at an initial temperature of 25°c and removed from the chamber at a safe-to-touch tempera ture of 37°c, what is the total elapsed time for the two-step curing operation?